點擊圖片查看大圖Rynite® FR945 BK507
THERMOPLASTIC POLYESTER RESIN
PET-(MD+GF)45 FR(17)
CHARACTERISTICS
Regional availability
- Global
Processing
Injection Molding
Additives
Flame retardant
Special characteristics
Heat stabilized or stable to heat, Flame retardant, Low Warpage
PRODUCT TEXT
Rynite® FR945 BK507 is a 45% Glass/Mineral Reinforced, Flame Retardant, Polyethylene Terephthalate
PRODUCT INFORMATION
VALUE
TEST NORM
Resin Identification
PET-(MD+GF)45FR(17)
ISO 1043
Part Marking Code
>PET-(MD+GF)45FR(17)<
ISO 11469
RHEOLOGICAL PROPERTIES
VALUE
UNIT
TEST NORM
Molding shrinkage, parallel
0.5
%
ISO 294-4, 2577
Molding shrinkage, normal
0.9
%
ISO 294-4, 2577
MECHANICAL PROPERTIES
VALUE
UNIT
TEST NORM
Tensile Modulus
12800
MPa
ISO 527-1/-2
Stress at break
92
MPa
ISO 527-1/-2
Strain at break
1.2
%
ISO 527-1/-2
Flexural Modulus
12500
MPa
ISO 178
Flexural Strength
140
MPa
ISO 178
Charpy impact strength, 73°F
20
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 73°F
4
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -40°F
3
kJ/m2
ISO 179/1eA
Izod notched impact strength, 73°F
4
kJ/m2
ISO 180/1A
Poisson's ratio
0.33
-
-
THERMAL PROPERTIES
VALUE
UNIT
TEST NORM
Melting temperature, 18°F/min
250
°C
ISO 11357-1/-3
Temp. of deflection under load, 260 psi
200
°C
ISO 75-1/-2
Temp. of deflection under load, 65 psi
240
°C
ISO 75-1/-2
RTI, electrical, 30mil
150
°C
UL 746B
RTI, electrical, 60mil
150
°C
UL 746B
RTI, electrical, 120mil
150
°C
UL 746B
RTI, impact, 30mil
150
°C
UL 746B
RTI, impact, 60mil
150
°C
UL 746B
RTI, impact, 120mil
150
°C
UL 746B
RTI, strength, 30mil
150
°C
UL 746B
RTI, strength, 60mil
150
°C
UL 746B
RTI, strength, 120mil
150
°C
UL 746B
FLAMMABILITY
VALUE
UNIT
TEST NORM
Burning Behav. at 60mil nom. thickn.
V-0
class
IEC 60695-11-10
Thickness tested
1.5
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. at thickness h
V-0
class
IEC 60695-11-10
Thickness tested
0.81
mm
IEC 60695-11-10
UL recognition
yes
-
UL 94
Burning Behav. 5V at thickness h
5VA
class
IEC 60695-11-20
Thickness tested
1.5
mm
IEC 60695-11-20
UL recognition
yes
-
UL 94
Glow Wire Flammability Index, 30mil
960
°C
IEC 60695-2-12
Glow Wire Flammability Index, 60mil
960
°C
IEC 60695-2-12
Glow Wire Flammability Index, 120mil
960
°C
IEC 60695-2-12
Glow Wire Ignition Temperature, 30mil
825
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 60mil
825
°C
IEC 60695-2-13
Glow Wire Ignition Temperature, 120mil
925
°C
IEC 60695-2-13
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
OTHER PROPERTIES
VALUE
UNIT
TEST NORM
Density
1850
kg/m3
ISO 1183
INJECTION
VALUE
UNIT
Drying Recommended
yes
Drying Temperature
120
°C
Drying Time, Dehumidified Dryer
4 - 6
h
Processing Moisture Content
≤0.021
%
Melt Temperature Optimum
280
°C
Min. melt temperature
270
°C
Max. melt temperature
290
°C
Max. screw tangential speed
0.2
m/s
Mold Temperature Optimum
110
°C
Min. mold temperature
100
°C
Max. mold temperature
1202
°C
Hold pressure range
≥80
MPa
Hold pressure time
4
s/mm
Back pressure
As low as possible
MPa
Ejection temperature
170
°C
1: At levels above 0.02%, strength and toughness will decrease, even though parts may not exhibit surface defects.
2: (6mm - 1mm thickness)