產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24hr,23℃ | ASTM D-570 | 0.20 | % | |
| 熔體流動(dòng)速率 | 300℃，1.2kg | ASTM D-1238 | 10 | g/10min | ||
| 物理性能 | 濁度 | 3.2mmt | ASTM D-1003 | ＜0.8 | % | |
| 比重 | 23/23℃ | ASTM D-792 | 1.20 | |||
| 全光穿透率 | 3mmt | ASTM D-570 | 89 | % | ||
| 機(jī)械性能 | 曲折率 | ASTM D-542 | 1.585 | % | ||
| 彎曲模數(shù) | 23℃ | ASTM D-790 | 24000 | kg/m2 | ||
| 壓縮強(qiáng)度 | ASTM D-695 | 780 | Kg/cm2 | |||
| IZOD缺口沖擊強(qiáng)度 | 1/8" | ASTM D-256 | 87 | kg.cm/cm | ||
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 920 | kg/m2 | ||
| 洛氏硬度 | ASTM D-785 | M-77 | M Scale | |||
| IZOD缺口沖擊強(qiáng)度 | 1/4" | ASTM D-256 | 14.3 | kg.cm/cm | ||
| 降伏引張強(qiáng)度 | 23℃ | ASTM D-638 | 630 | kg/m2 | ||
| 延伸率 | 降伏點(diǎn) | 23℃ | ASTM D-638 | 6 | ℃ | |
| 破裂點(diǎn) | 23℃ | ASTM D-638 | 110 | ℃ | ||
| 電氣性能 | 體積電阻率 | ASTM D-257 | 3 | ×1016Ω.cm | ||
| 耐電弧性 | ASTM D-495 | 110 | Sec | |||
| 絕緣破壞強(qiáng)度 | 1.6mm | ASTM D-149 | 30 | KV/mm | ||
| 介電損耗 | 60Hz | ASTM D-150 | 0.0004 | |||
| 介電常數(shù) | 60Hz | ASTM D-150 | 2.95 | |||
| 介電常數(shù) | 106Hz | ASTM D-150 | 2.9 | |||
| 介電損耗 | 106Hz | ASTM D-150 | 0.009 | |||
| 加工性能 | 成型收縮率 | Parallel | ASTM D-955 | 0.5-0.7 | % | |
| 成型收縮率 | Across | ASTM D-955 | 0.5-0.7 | % | ||
| 熱性能 | 熱傳導(dǎo)系數(shù) | ASTM C-177 | 0.2 | W/m℃ | ||
| 熱變形溫度 | 未退火,18.6Kg/cm2,120℃ | ASTM D-648 | 125 | ℃ | ||
| 熱變形溫度 | 未退火,4.6Kg/cm2,120℃ | ASTM D-648 | 136 | ℃ | ||
| 線膨脹系數(shù) | 40～100℃ | ASTM D-696 | 6-8 | ×10-5cm/cm/℃ | ||
| 燃燒性 | 1/16" | UL 94 | V-2 | |||
| 維卡軟化點(diǎn) | 1Kg,50℃/hr | ASTM D-1525 | 153 | ℃ | ||
產(chǎn)品細(xì)節(jié)圖
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。